Injection Moulding and Sintering of Ceria Ceramics

MACA, K., TRUNEC, M., CIHLÁŘ, J.

Originální název

Injection Moulding and Sintering of Ceria Ceramics

Anglický název

Injection Moulding and Sintering of Ceria Ceramics

Druh

Článek recenzovaný mimo WoS a Scopus

Originální abstrakt

Ceria powder was dry-milled to sub-micrometric particle sizes and used in the preparation of ceramic mixture for injection moulding. Specimen bodies were injection moulded in the shape of rectangular bars. The sintering kinetics of these bodies was studied in a dilatometer under various sintering conditions and also by the rate-controlled sintering method. Sintering the injection moulded CeO2 to a density of 7.08 g.cm-3 (99.3% TD) was possible already at a temperature of 1400C, and the highest density value (99.8% TD) was obtained at a heating rate of 2C.min-1 and a holding time of 1 hour at 1500C. Using heating rates of over 5C.min-1 had an adverse effect on the density obtained. Applying the rate-controlled sintering (RCS) method did not lead to any decrease in the grain size if compared with temperature-controlled sintering (TCS).

Anglický abstrakt

Ceria powder was dry-milled to sub-micrometric particle sizes and used in the preparation of ceramic mixture for injection moulding. Specimen bodies were injection moulded in the shape of rectangular bars. The sintering kinetics of these bodies was studied in a dilatometer under various sintering conditions and also by the rate-controlled sintering method. Sintering the injection moulded CeO2 to a density of 7.08 g.cm-3 (99.3% TD) was possible already at a temperature of 1400C, and the highest density value (99.8% TD) was obtained at a heating rate of 2C.min-1 and a holding time of 1 hour at 1500C. Using heating rates of over 5C.min-1 had an adverse effect on the density obtained. Applying the rate-controlled sintering (RCS) method did not lead to any decrease in the grain size if compared with temperature-controlled sintering (TCS).

Klíčová slova

ceria, injection moulding, sintering

Klíčová slova v angličtině

ceria, injection moulding, sintering

Autoři

MACA, K., TRUNEC, M., CIHLÁŘ, J.

Rok RIV

2011

Vydáno

01.01.2002

Nakladatel

Elsevier

ISSN

0272-8842

Periodikum

Ceramics International

Svazek

28

Číslo

3

Stát

Spojené království Velké Británie a Severního Irska

Strany od

337

Strany počet

8

Plný text v Digitální knihovně

http://hdl.handle.net/

BibTex

@article{BUT40426,
  author="Karel {Maca} and Martin {Trunec} and Jaroslav {Cihlář}",
  title="Injection Moulding and Sintering of Ceria Ceramics",
  journal="Ceramics International",
  year="2002",
  volume="28",
  number="3",
  pages="8",
  issn="0272-8842"
}