Detail publikačního výsledku

A fracture mechanics assessment of surface cracks existing in protective layers of multilayer composite pipes

HUTAŘ, P.; NÁHLÍK, L.; ŠESTÁKOVÁ, L.; ŠEVČÍK, M.; KNÉSL, Z.; NEZBEDOVÁ, E.

Originální název

A fracture mechanics assessment of surface cracks existing in protective layers of multilayer composite pipes

Anglický název

A fracture mechanics assessment of surface cracks existing in protective layers of multilayer composite pipes

Druh

Článek recenzovaný mimo WoS a Scopus

Originální abstrakt

The influence of cracked protective layer on the integrity of composite multilayer pipes is analysed in this paper. The multilayer pipe is modeled as a particular case of a bi-material body consisting of two different homogeneous materials. The problem is studied under assumptions corresponding to small scale yielding conditions and ideal adhesion between protective and main layers is assumed. The case of a crack with its tip at the interface between protective and main layers is analyzed in details and the influence of the material composition on the corresponding critical pressure for a brittle-like failure is discussed. An approximate approach based on estimation of crack mouth opening displacement for thin protective layers is suggested. The results can be applied to study of scratch resistance of multi-layered plastic pipes.

Anglický abstrakt

The influence of cracked protective layer on the integrity of composite multilayer pipes is analysed in this paper. The multilayer pipe is modeled as a particular case of a bi-material body consisting of two different homogeneous materials. The problem is studied under assumptions corresponding to small scale yielding conditions and ideal adhesion between protective and main layers is assumed. The case of a crack with its tip at the interface between protective and main layers is analyzed in details and the influence of the material composition on the corresponding critical pressure for a brittle-like failure is discussed. An approximate approach based on estimation of crack mouth opening displacement for thin protective layers is suggested. The results can be applied to study of scratch resistance of multi-layered plastic pipes.

Klíčová slova

protective layers, multilayer pipes damage, fracture mechanics, bi-material interface, generalized stress intensity factor

Klíčová slova v angličtině

protective layers, multilayer pipes damage, fracture mechanics, bi-material interface, generalized stress intensity factor

Autoři

HUTAŘ, P.; NÁHLÍK, L.; ŠESTÁKOVÁ, L.; ŠEVČÍK, M.; KNÉSL, Z.; NEZBEDOVÁ, E.

Rok RIV

2012

Vydáno

09.10.2009

Nakladatel

Elsevier

Místo

Amsterdam, Nizozemí

ISSN

0263-8223

Periodikum

COMPOSITE STRUCTURES

Svazek

92

Číslo

5

Stát

Spojené království Velké Británie a Severního Irska

Strany od

1120

Strany do

1125

Strany počet

6

BibTex

@article{BUT49609,
  author="Pavel {Hutař} and Luboš {Náhlík} and Lucie {Malíková} and Martin {Ševčík} and Zdeněk {Knésl} and Eva {Nezbedová}",
  title="A fracture mechanics assessment of surface cracks existing in protective layers of multilayer composite pipes",
  journal="COMPOSITE STRUCTURES",
  year="2009",
  volume="92",
  number="5",
  pages="1120--1125",
  issn="0263-8223"
}