COMPARISON OF MECHANICAL AND PHYSICAL CHARACTERISTICS OF THE LIGHTWEIGHT CONCRETE WITH AND WITHOUT FIBRES
KUCHARCZYKOVÁ, B. PLŠKOVÁ, I. ADÁMEK, J.
Originální název
COMPARISON OF MECHANICAL AND PHYSICAL CHARACTERISTICS OF THE LIGHTWEIGHT CONCRETE WITH AND WITHOUT FIBRES
Anglický název
COMPARISON OF MECHANICAL AND PHYSICAL CHARACTERISTICS OF THE LIGHTWEIGHT CONCRETE WITH AND WITHOUT FIBRES
Jazyk
en
Originální abstrakt
The contribution presents results from destructive and non-destructive experimental tests on specimens from lightweight concrete with fibres, which are compared with tests results on specimens from lightweight concrete without fibres. As an aggregate an inland-made porous aggregates Liapor and heavy-weight aggregates with maximal grains of 8 mm was used. According to CSN P ENV 206 the reference concrete conform to the grade of concrete LC 45/50 with density 1800 kg/m3. As a dispersed reinforcement a polypropylene fibres Forta Ferro of 54 mm length and tensile strength of 620 - 758 MPa was used.
Anglický abstrakt
The contribution presents results from destructive and non-destructive experimental tests on specimens from lightweight concrete with fibres, which are compared with tests results on specimens from lightweight concrete without fibres. As an aggregate an inland-made porous aggregates Liapor and heavy-weight aggregates with maximal grains of 8 mm was used. According to CSN P ENV 206 the reference concrete conform to the grade of concrete LC 45/50 with density 1800 kg/m3. As a dispersed reinforcement a polypropylene fibres Forta Ferro of 54 mm length and tensile strength of 620 - 758 MPa was used.
Dokumenty
BibTex
@inproceedings{BUT22676,
author="Barbara {Kucharczyková} and Iveta {Plšková} and Jiří {Adámek}",
title="COMPARISON OF MECHANICAL AND PHYSICAL CHARACTERISTICS OF THE LIGHTWEIGHT CONCRETE WITH AND WITHOUT FIBRES",
annote="The contribution presents results from destructive and non-destructive experimental tests on specimens from lightweight concrete with fibres, which are compared with tests results on specimens from lightweight concrete without fibres. As an aggregate an inland-made porous aggregates Liapor and heavy-weight aggregates with maximal grains of 8 mm was used. According to CSN P ENV 206 the reference concrete conform to the grade of concrete LC 45/50 with density 1800 kg/m3. As a dispersed reinforcement a polypropylene fibres Forta Ferro of 54 mm length and tensile strength of 620 - 758 MPa was used.",
booktitle="Proceedings of 4th International Conference Fibre Concrete 2007",
chapter="22676",
edition="ČVUT v Praze",
year="2007",
month="september",
pages="67--72",
type="conference paper"
}