Evaluation of Cold Kinetic Deposition Technology

Evaluation of Cold Kinetic Deposition Technology

Stať ve sborníku mimo WoS a Scopus

This article deals with the possibility of using cold spray technology. For the basic sample, an aluminum plate was used as a substrate, on which a layer of copper was subsequently formed. The samples were equipped with an acoustic emission measurement sensor and were placed in a condensation chamber, where the formation of corrosion was evaluated. Corrosion testing took place in a condensation chamber under steady conditions at a temperature of 50 °C and relative humidity 100%. The samples were exposed to the internal environment of the chamber for a given time, while continuous acoustic emission measurements were performed on them. A metallographic test was performed on the individual samples after the end of the given time cycle of the test

This article deals with the possibility of using cold spray technology. For the basic sample, an aluminum plate was used as a substrate, on which a layer of copper was subsequently formed. The samples were equipped with an acoustic emission measurement sensor and were placed in a condensation chamber, where the formation of corrosion was evaluated. Corrosion testing took place in a condensation chamber under steady conditions at a temperature of 50 °C and relative humidity 100%. The samples were exposed to the internal environment of the chamber for a given time, while continuous acoustic emission measurements were performed on them. A metallographic test was performed on the individual samples after the end of the given time cycle of the test

cold spray, corrosion, condensation chamber

cold spray, corrosion, condensation chamber

ŠAFL, P.; ZIMÁKOVÁ, J.; BINAR, T.; ČUDEK, P.

31.07.2022

Brno University of Technology

Brno

978-80-214-6088-1

Advanced Batteries Accumulators and Fuel Cells – 23rd ABAF

1

215

217

3

https://www.aba-brno.cz/download/2022-ABAF-Proceeding.pdf

http://hdl.handle.net/