Rapid pressure-less and spark plasma sintering of (Ba0.85Ca0.15Zr0.1T0.9)O3 lead-free piezoelectric ceramics

BIJALWAN, V.; PRAJZLER, V.; ERHART, J.; TAN, H.; ROUPCOVÁ, P.; SOBOLA, D.; TOFEL, P.; MACA, K.

Originální název

Rapid pressure-less and spark plasma sintering of (Ba0.85Ca0.15Zr0.1T0.9)O3 lead-free piezoelectric ceramics

Anglický název

Rapid pressure-less and spark plasma sintering of (Ba0.85Ca0.15Zr0.1T0.9)O3 lead-free piezoelectric ceramics

Druh

Článek WoS

Originální abstrakt

This work shows for the first time the possibility to sinter BCZT powder compacts by rapid heating rates within one hour of sintering, while achieving good piezoelectric properties. The sintering was performed by rapid (heating rates 100 and 200 °C/min) pressure-less sintering (PLS) at 1550 °C/5-60 min and by SPS sintering (100 °C/min, 1450 °C/5−60 min and 1500 °C/15−45 min). The rapid PLS samples reached a relative density up to 94 % and grain sizes of 17–36 μm acquiring d33 up to 414 pC/N. Although the SPS samples reached full density at 1450 °C, their piezoelectric properties worsened due to smaller grains (10−15 μm) as well as formation of cracks at dwell times > 30 min. At elevated SPS temperature of 1500 °C/30 min, the d33 increased to 360 pC/N sustaining full density. Even higher increase in d33 (424 pC/N) of SPS samples was achieved by post-rapid PLS at 1550 °C/60 min resulting from further expansion in grain size.

Anglický abstrakt

This work shows for the first time the possibility to sinter BCZT powder compacts by rapid heating rates within one hour of sintering, while achieving good piezoelectric properties. The sintering was performed by rapid (heating rates 100 and 200 °C/min) pressure-less sintering (PLS) at 1550 °C/5-60 min and by SPS sintering (100 °C/min, 1450 °C/5−60 min and 1500 °C/15−45 min). The rapid PLS samples reached a relative density up to 94 % and grain sizes of 17–36 μm acquiring d33 up to 414 pC/N. Although the SPS samples reached full density at 1450 °C, their piezoelectric properties worsened due to smaller grains (10−15 μm) as well as formation of cracks at dwell times > 30 min. At elevated SPS temperature of 1500 °C/30 min, the d33 increased to 360 pC/N sustaining full density. Even higher increase in d33 (424 pC/N) of SPS samples was achieved by post-rapid PLS at 1550 °C/60 min resulting from further expansion in grain size.

Klíčová slova

Lead-free piezoceramics; Microstructure; Piezoelectric constant; Rapid pressure-less sintering; SPS

Klíčová slova v angličtině

Lead-free piezoceramics; Microstructure; Piezoelectric constant; Rapid pressure-less sintering; SPS

Autoři

BIJALWAN, V.; PRAJZLER, V.; ERHART, J.; TAN, H.; ROUPCOVÁ, P.; SOBOLA, D.; TOFEL, P.; MACA, K.

Rok RIV

2021

Vydáno

01.04.2021

ISSN

0955-2219

Periodikum

Journal of the European Ceramic Society

Svazek

41

Číslo

4

Stát

Spojené království Velké Británie a Severního Irska

Strany od

2514

Strany do

2523

Strany počet

10

URL

https://www.sciencedirect.com/science/article/pii/S0955221920309286?via%3Dihub

BibTex

@article{BUT169317,
  author="Vijay {Bijalwan} and Vladimír {Prajzler} and Jiří {Erhart} and Hua {Tan} and Pavla {Roupcová} and Dinara {Sobola} and Pavel {Tofel} and Karel {Maca}",
  title="Rapid pressure-less and spark plasma sintering of (Ba0.85Ca0.15Zr0.1T0.9)O3 lead-free piezoelectric ceramics",
  journal="Journal of the European Ceramic Society",
  year="2021",
  volume="41",
  number="4",
  pages="2514--2523",
  doi="10.1016/j.jeurceramsoc.2020.11.029",
  issn="0955-2219",
  url="https://www.sciencedirect.com/science/article/pii/S0955221920309286?via%3Dihub"
}