DEGRADATION OF TURBINE BLADE MADE OF SUPERALLOY ZHS6K DURING SERVICE

NĚMEC, K.; PODRÁBSKÝ, T.; HAKL, J.; VLASÁK, T.; MAN, O.

Originální název

DEGRADATION OF TURBINE BLADE MADE OF SUPERALLOY ZHS6K DURING SERVICE

Anglický název

DEGRADATION OF TURBINE BLADE MADE OF SUPERALLOY ZHS6K DURING SERVICE

Druh

Stať ve sborníku v databázi WoS či Scopus

Originální abstrakt

It is an important technical and economic requirement to increase the service life of gas turbines while keeping their reliability and safety. For this reason, critical parts removed after finish of service in turbine are analyzed for damage and degradation of materials and the level of service life exhaustion is assessed.

Anglický abstrakt

It is an important technical and economic requirement to increase the service life of gas turbines while keeping their reliability and safety. For this reason, critical parts removed after finish of service in turbine are analyzed for damage and degradation of materials and the level of service life exhaustion is assessed.

Klíčová slova v angličtině

Turbine blade, Ni-base superalloy, Structure

Autoři

NĚMEC, K.; PODRÁBSKÝ, T.; HAKL, J.; VLASÁK, T.; MAN, O.

Vydáno

27.01.2005

Místo

Žilina

ISBN

80-8070-344-2

Kniha

SEMDOK 2005

Edice

1

Strany od

63

Strany počet

4

BibTex

@inproceedings{BUT15762,
  author="Karel {Němec} and Tomáš {Podrábský} and Jan {Hakl} and Tomáš {Vlasák} and Ondřej {Man}",
  title="DEGRADATION OF TURBINE BLADE MADE OF SUPERALLOY ZHS6K DURING SERVICE",
  booktitle="SEMDOK 2005",
  year="2005",
  series="1",
  number="1",
  pages="4",
  address="Žilina",
  isbn="80-8070-344-2"
}