Modification of poly(lactic acid) by radical grafting for application in advanced polymeric materials

KUČERA, F.; PETRUŠ, J.

Originální název

Modification of poly(lactic acid) by radical grafting for application in advanced polymeric materials

Anglický název

Modification of poly(lactic acid) by radical grafting for application in advanced polymeric materials

Druh

Stať ve sborníku v databázi WoS či Scopus

Originální abstrakt

Post-reactor modification of poly(lactic acid) (PLA) was realized by free-radical grafting of PLA with itaconic anhydride (IAH) which are both derived from renewable resources. The reaction was initiated using 2,5-dimethyl-2,5-bis(tert-butylperoxy)hexane (L-101). The influence of reaction conditions on IAH conversion, thermal properties and material structure was investigated. Hydrolytic scission of backbone or IAH homopolymerization was observed as undesired reactions. Evidence of grafted IAH and relation between reaction conversion and IAH/L-101 ratio were confirmed by acid-base titration, FTIR spectroscopy and NMR spectroscopy. Thermal properties and crystallization behavior of neat PLA and modified PLA (i.e, Tg, Xc) were determined as a function of monomer conversion by temperature modulated scanning calorimetry - TMDSC. Molecular weight and polydisperzity of grafted PLA samples were determined by GPC, contact angle was measured to predict adhesion properties.

Anglický abstrakt

Post-reactor modification of poly(lactic acid) (PLA) was realized by free-radical grafting of PLA with itaconic anhydride (IAH) which are both derived from renewable resources. The reaction was initiated using 2,5-dimethyl-2,5-bis(tert-butylperoxy)hexane (L-101). The influence of reaction conditions on IAH conversion, thermal properties and material structure was investigated. Hydrolytic scission of backbone or IAH homopolymerization was observed as undesired reactions. Evidence of grafted IAH and relation between reaction conversion and IAH/L-101 ratio were confirmed by acid-base titration, FTIR spectroscopy and NMR spectroscopy. Thermal properties and crystallization behavior of neat PLA and modified PLA (i.e, Tg, Xc) were determined as a function of monomer conversion by temperature modulated scanning calorimetry - TMDSC. Molecular weight and polydisperzity of grafted PLA samples were determined by GPC, contact angle was measured to predict adhesion properties.

Klíčová slova

poly(lactic acid); radical grafting; itaconic anhydride;

Klíčová slova v angličtině

poly(lactic acid); radical grafting; itaconic anhydride;

Autoři

KUČERA, F.; PETRUŠ, J.

Vydáno

01.06.2014

ISBN

978-80-86238-64-7

Kniha

Proceedings of the 2nd International Conference on Chemical Technology

Edice

1st

Strany od

309

Strany do

315

Strany počet

7

BibTex

@inproceedings{BUT112187,
  author="František {Kučera} and Josef {Petruš}",
  title="Modification of poly(lactic acid) by radical grafting for application in advanced polymeric materials",
  booktitle="Proceedings of the 2nd International Conference on Chemical Technology",
  year="2014",
  series="1st",
  pages="309--315",
  isbn="978-80-86238-64-7"
}