Three-Dimensional Modelling of Intergranular Fracture

POKLUDA, J., ŠANDERA, P.

Originální název

Three-Dimensional Modelling of Intergranular Fracture

Anglický název

Three-Dimensional Modelling of Intergranular Fracture

Druh

Stať ve sborníku v databázi WoS či Scopus

Originální abstrakt

A computer based 3D model of stable intergranular crack is developed. It simulates experimental and practical conditions occuring in fatigue, brittle fracture and stress corrosion cracking cases. Creation of the intergranular crack is constructed according to some geometrically justified rules. This procedure reflects well the real damage process and allows us to quantify the geometrically induced crack tip shielding due to the branched crack fro

Anglický abstrakt

A computer based 3D model of stable intergranular crack is developed. It simulates experimental and practical conditions occuring in fatigue, brittle fracture and stress corrosion cracking cases. Creation of the intergranular crack is constructed according to some geometrically justified rules. This procedure reflects well the real damage process and allows us to quantify the geometrically induced crack tip shielding due to the branched crack fro

Klíčová slova v angličtině

computer modelling, Voronoi tesselation, intergranular surface, crack branching

Autoři

POKLUDA, J., ŠANDERA, P.

Vydáno

06.09.1999

Nakladatel

TU Košice

Místo

Herľany, Slovenská republika

ISBN

80-7099-43

Kniha

Physical Metallurgy and Fracture of Materials '99

Strany od

63

Strany počet

4

BibTex

@inproceedings{BUT501,
  author="Jaroslav {Pokluda} and Pavel {Šandera}",
  title="Three-Dimensional Modelling of Intergranular Fracture",
  booktitle="Physical Metallurgy and Fracture of Materials '99",
  year="1999",
  pages="4",
  publisher="TU Košice",
  address="Herľany, Slovenská republika",
  isbn="80-7099-43"
}