Processing and properties of fine-grained transparent MgAl2O4 ceramics

MACA, K.; TRUNEC, M.; CHMELÍK, R.

Originální název

Processing and properties of fine-grained transparent MgAl2O4 ceramics

Anglický název

Processing and properties of fine-grained transparent MgAl2O4 ceramics

Druh

Článek WoS

Originální abstrakt

Transparent fine-grained MgAl2O4 ceramics was prepared from nanometre-sized powder without any sintering additives. Ceramic green bodies were prepared by cold isostatic pressing and then pressureless presintered at temperatures of 1550-1600degC to reach closed porosity. Presintered samples were subsequently hot isostatically pressed (HIPed) at 1500degC and 200 MPa for 1 hour. The final density as well as the transparency of HIPed samples was affected by presintering densities. The highest final density (~100% t.d.) and highest in-line transmission (60.2% for sample thickness 1.1mm and = 632.8 nm) were obtained for sample presintered to the lowest density value still guaranteeing the structure with closed porosity (~94% t.d.). The HIPed sample had an average grain size of 1 micron and hardness HV=13.0 GPa.

Anglický abstrakt

Transparent fine-grained MgAl2O4 ceramics was prepared from nanometre-sized powder without any sintering additives. Ceramic green bodies were prepared by cold isostatic pressing and then pressureless presintered at temperatures of 1550-1600degC to reach closed porosity. Presintered samples were subsequently hot isostatically pressed (HIPed) at 1500degC and 200 MPa for 1 hour. The final density as well as the transparency of HIPed samples was affected by presintering densities. The highest final density (~100% t.d.) and highest in-line transmission (60.2% for sample thickness 1.1mm and = 632.8 nm) were obtained for sample presintered to the lowest density value still guaranteeing the structure with closed porosity (~94% t.d.). The HIPed sample had an average grain size of 1 micron and hardness HV=13.0 GPa.

Klíčová slova

spinel ceramics, sintering, hot-isostatic pressing, microstructure, optical properties

Klíčová slova v angličtině

spinel ceramics, sintering, hot-isostatic pressing, microstructure, optical properties

Autoři

MACA, K.; TRUNEC, M.; CHMELÍK, R.

Rok RIV

2011

Vydáno

01.01.2007

Nakladatel

Institute of Chemical Technology in Prague and Academy of Sciences of the Czech Republic

Místo

Prague

ISSN

0862-5468

Periodikum

CERAMICS-SILIKATY

Svazek

51

Číslo

2

Stát

Česká republika

Strany od

94

Strany do

97

Strany počet

4

BibTex

@article{BUT44028,
  author="Karel {Maca} and Martin {Trunec} and Radim {Chmelík}",
  title="Processing and properties of fine-grained transparent MgAl2O4 ceramics",
  journal="CERAMICS-SILIKATY",
  year="2007",
  volume="51",
  number="2",
  pages="94--97",
  issn="0862-5468"
}