This research focuses on the comprehensive investigation and quantification of fatigue behavior in HSSs under varied conditions. Key areas of study include evaluating fatigue performance in welded joints and analyzing the impact of defects (weld, corrosion) on fatigue life. Defect parameters are determined using tomographic data, linking geometry to fatigue behavior. The findings provide insights into optimizing design and durability of HSS components, particularly under cyclic loading.

FAST-S-25-8839

čeština

Seitl Stanislav, prof. Ing., Ph.D. - hlavní řešitel
Al Khazali Mohammad Sami, Ing. - spoluřešitel

Ústav stavební mechaniky
- interní (1.1.2025 - 31.12.2025)
Fakulta stavební
- příjemce (1.1.2025 - 31.12.2025)

AL KHAZALI, M.; SEITL, S.; MALÍKOVÁ, L.; KRIVY, V.; VACEK, M. Effect of corrosion damage on the fatigue behavior of S460NL High-Strength Steel under cyclic loading. Fracture and structural integrity, 2026, iss. 20(77), p. 56-70.
Detail

DOUBEK, P.; KOZAKOVA, K.; HORNIK, V.; KUNZ, L.; SEITL, S. Fatigue life of AISI P20+ Ni steel with an Al-bronze surface layer applied by laser cladding. Materials Today Communications, 2026, iss. 55, p. 1-7.
Detail

AL KHAZALI, M.; MALÍKOVÁ, L.; LESIUK, G.; SEITL, S. Fatigue Performance of S460 High-Strength Steel Welded Joints: Experimental and Numerical Approaches. In Lecture Notes in Civil Engineering, Structural and Physical Aspects of Construction Engineering. Cham: Springer Nature Switzerland, 2026. p. 346.ISBN: 9783032250650.
Detail

Odpovědnost: Seitl Stanislav, prof. Ing., Ph.D.