Cold isostatic pressing and sintering of alumina and zirconia nanoceramics

MACA, K., TRUNEC, M., DOBŠÁK, P.

Originální název

Cold isostatic pressing and sintering of alumina and zirconia nanoceramics

Anglický název

Cold isostatic pressing and sintering of alumina and zirconia nanoceramics

Druh

Stať ve sborníku v databázi WoS či Scopus

Originální abstrakt

The influence of particle size and compacting pressure on the microstructure and sinterability of ceramic green bodies were studied. Alumina and zirconia powders with particle size smaller than 35 nm were used and their behaviour was compared with submicrometre sized powders. The green bodies were prepared by cold isostatic pressing at 300, 700 and 1000 MPa. The open porosity of pressed samples was evaluated by mercury intrusion. Specimens were sintered in high temperature dilatometer. The microstructure was examined using electron microscopy. In the case of zirconia ceramics the sintering temperature decreased with decreasing particle size and with increasing compacting pressure. Zirconia nanoceramics exhibited final microstructure with grain size below 80 nm and density exceeding 99 % of theoretical density after sintering at 1100°C. Alumina samples made of nanopowders showed poor sinterability probably due to high level of powder agglomeration.

Anglický abstrakt

The influence of particle size and compacting pressure on the microstructure and sinterability of ceramic green bodies were studied. Alumina and zirconia powders with particle size smaller than 35 nm were used and their behaviour was compared with submicrometre sized powders. The green bodies were prepared by cold isostatic pressing at 300, 700 and 1000 MPa. The open porosity of pressed samples was evaluated by mercury intrusion. Specimens were sintered in high temperature dilatometer. The microstructure was examined using electron microscopy. In the case of zirconia ceramics the sintering temperature decreased with decreasing particle size and with increasing compacting pressure. Zirconia nanoceramics exhibited final microstructure with grain size below 80 nm and density exceeding 99 % of theoretical density after sintering at 1100°C. Alumina samples made of nanopowders showed poor sinterability probably due to high level of powder agglomeration.

Klíčová slova

zirconia, alumina, bulk nanoceramics

Klíčová slova v angličtině

zirconia, alumina, bulk nanoceramics

Autoři

MACA, K., TRUNEC, M., DOBŠÁK, P.

Rok RIV

2011

Vydáno

01.01.2004

Nakladatel

VUTIUM

Místo

Brno

ISBN

80-214-2793-0

Kniha

Proceedings of the International Conference NAN0 '04

Strany od

91

Strany počet

6

BibTex

@inproceedings{BUT13042,
  author="Karel {Maca} and Martin {Trunec} and Petr {Dobšák}",
  title="Cold isostatic pressing and sintering of alumina and zirconia nanoceramics",
  booktitle="Proceedings of the International Conference NAN0 '04",
  year="2004",
  pages="6",
  publisher="VUTIUM",
  address="Brno",
  isbn="80-214-2793-0"
}