Detail publikačního výsledku

Influence of Microstructural parameters on the Corrosion Resistance of Aluminium Alloy BS L170

HORYNOVÁ, M.; KLAKURKOVÁ, L.; JULIŠ, M.; GEJDOŠ, P.; ČELKO, L.

Originální název

Influence of Microstructural parameters on the Corrosion Resistance of Aluminium Alloy BS L170

Anglický název

Influence of Microstructural parameters on the Corrosion Resistance of Aluminium Alloy BS L170

Druh

Abstrakt

Originální abstrakt

The aim of this analysis was to identify the cause of poor corrosion resistance of final product, after the slight change of heat treatment of initial material. Although the hardness of material prior and after the change was the same, significant difference in microstructure was revealed by microstructural analysis. Change in heat treatment process lead to heterogeneous distribution of precipitates and increase in the precipitate size which caused deterioration in corrosion resistance. Based on the findings, further optimization of heat treatment was suggested. More importantly, initial material inspection based on microstructural analysis, not only mechanical testing, was recommended. recommended.

Anglický abstrakt

The aim of this analysis was to identify the cause of poor corrosion resistance of final product, after the slight change of heat treatment of initial material. Although the hardness of material prior and after the change was the same, significant difference in microstructure was revealed by microstructural analysis. Change in heat treatment process lead to heterogeneous distribution of precipitates and increase in the precipitate size which caused deterioration in corrosion resistance. Based on the findings, further optimization of heat treatment was suggested. More importantly, initial material inspection based on microstructural analysis, not only mechanical testing, was recommended. recommended.

Klíčová slova

corrosion resistance; aluminium alloy,; heterogeneity; heat treatment

Klíčová slova v angličtině

corrosion resistance; aluminium alloy,; heterogeneity; heat treatment

Autoři

HORYNOVÁ, M.; KLAKURKOVÁ, L.; JULIŠ, M.; GEJDOŠ, P.; ČELKO, L.

Rok RIV

2017

Vydáno

19.04.2016

Nakladatel

Faculty of Metallurgy Technical University of Košice

Místo

Košice

ISBN

978-80-553-2547-7

Kniha

Metallography ´16

Strany od

98

Strany do

98

Strany počet

1

BibTex

@misc{BUT127035,
  author="Miroslava {Horynová} and Lenka {Klakurková} and Martin {Juliš} and Pavel {Gejdoš} and Ladislav {Čelko}",
  title="Influence of Microstructural parameters on the Corrosion Resistance of Aluminium Alloy BS L170",
  booktitle="Metallography ´16",
  year="2016",
  edition="1",
  pages="98--98",
  publisher="Faculty of Metallurgy Technical University of Košice",
  address="Košice",
  isbn="978-80-553-2547-7",
  note="Abstract"
}