High Cycle Fatigue Damage Mechanisms of MAR-M 247 Superalloy at High Temperatures

ŠMÍD, M. HORNÍK, V. HUTAŘ, P. KUNZ, L. HRBÁČEK, K.

Originální název

High Cycle Fatigue Damage Mechanisms of MAR-M 247 Superalloy at High Temperatures

Typ

článek v časopise ve Web of Science, Jimp

Jazyk

angličtina

Originální abstrakt

High cycle fatigue tests of the MAR-M 247 superalloy under constant load were conducted with the aim to determine S–N curves at temperatures 650, 800, 900 and 950 °C. It has been found that the slope of the S–N curves reflects changes of the cyclic deformation mechanism with temperature. At temperatures 650 and partly at 800 °C, fatigue crack propagation exhibits crystallographic character (propagation along the {111} system) in early stages of the fatigue life. The crystallographic mode of the fatigue crack propagation was found to disappear at temperatures 900 and 950 °C.

Klíčová slova

High cycle fatigue; S–N curves; Fractography; High temperature; EBSD analysis

Autoři

ŠMÍD, M.; HORNÍK, V.; HUTAŘ, P.; KUNZ, L.; HRBÁČEK, K.

Vydáno

7. 1. 2016

Nakladatel

Springer India

ISSN

0972-2815

Periodikum

TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS

Ročník

69

Číslo

2

Stát

Indická republika

Strany od

393

Strany do

397

Strany počet

5

URL

http://link.springer.com/article/10.1007%2Fs12666-015-0817-0

BibTex

@article{BUT121180,
  author="Miroslav {Šmíd} and Vít {Horník} and Pavel {Hutař} and Ludvík {Kunz} and Karel {Hrbáček}",
  title="High Cycle Fatigue Damage Mechanisms of MAR-M 247 Superalloy at High Temperatures",
  journal="TRANSACTIONS OF THE INDIAN INSTITUTE OF METALS",
  year="2016",
  volume="69",
  number="2",
  pages="393--397",
  doi="10.1007/s12666-015-0817-0",
  issn="0972-2815",
  url="http://link.springer.com/article/10.1007%2Fs12666-015-0817-0"
}