Fatigue Fracture of Turbine Blades: Case Studies

KIANICOVÁ, M.; POKLUDA, J.

Originální název

Fatigue Fracture of Turbine Blades: Case Studies

Anglický název

Fatigue Fracture of Turbine Blades: Case Studies

Druh

Článek WoS

Originální abstrakt

Fracture surfaces of two sets of rotor blades failed after strong testing procedures of aircraft engines in the test-stand are investigated by means of SEM. While the process of fatigue fracture in the first set of blades did not reveal any defect features, both the initiation and propagation of fatigue cracks was strongly influenced by casting defects

Anglický abstrakt

Fracture surfaces of two sets of rotor blades failed after strong testing procedures of aircraft engines in the test-stand are investigated by means of SEM. While the process of fatigue fracture in the first set of blades did not reveal any defect features, both the initiation and propagation of fatigue cracks was strongly influenced by casting defects

Klíčová slova

Turbine blades; failure analysis; fatigue fracture; casting defects

Klíčová slova v angličtině

Turbine blades; failure analysis; fatigue fracture; casting defects

Autoři

KIANICOVÁ, M.; POKLUDA, J.

Rok RIV

2015

Vydáno

31.01.2014

Nakladatel

Trans Tech Publications

Místo

Bern

ISSN

1013-9826

Periodikum

Key Engineering Materials (print)

Svazek

592-593

Číslo

1

Stát

Švýcarská konfederace

Strany od

712

Strany do

715

Strany počet

4

BibTex

@article{BUT110139,
  author="Marta {Kianicová} and Jaroslav {Pokluda}",
  title="Fatigue Fracture of Turbine Blades: Case Studies",
  journal="Key Engineering Materials (print)",
  year="2014",
  volume="592-593",
  number="1",
  pages="712--715",
  doi="10.4028/www.scientific.net/KEM.592-593.712",
  issn="1013-9826"
}