Corrosion resistance and other utility properties of selected austenitic nodular cast irons

Corrosion resistance and other utility properties of selected austenitic nodular cast irons

Paper in proceedings (conference paper)

This study deals with the evaluation of corrosion resistance and other utility properties of selected austenitic nodular cast irons and their comparison with other (non-austenitic) nodular cast irons. For the investigations, two types of austenitic nodular cast iron were selected: nickel-manganese nodular cast iron EN-GJSA-XNiMn13-7 and nickel-chromium nodular cast iron EN-GJSA-XNiCr20-2. Basic mechanical properties, such as yield strength, tensile strength, elongation, absorbed energy and hardness, were evaluated using mechanical tests. The fatigue limit was determined using low-frequency fatigue tests. Corrosion properties, such as average corrosion rate, corrosion potential and corrosion current density, were determined by the exposure immersion test and the electrochemical potentiodynamic polarisation test. Both corrosion tests were performed in a 3.5% NaCl solution (to simulate seawater) at room temperature. The results of mechanical, fatigue and corrosion tests show that austenitic nodular cast irons have lower strength and fatigue properties but significantly higher plastic properties and corrosion resistance compared to non-austenitic nodular cast irons.

This study deals with the evaluation of corrosion resistance and other utility properties of selected austenitic nodular cast irons and their comparison with other (non-austenitic) nodular cast irons. For the investigations, two types of austenitic nodular cast iron were selected: nickel-manganese nodular cast iron EN-GJSA-XNiMn13-7 and nickel-chromium nodular cast iron EN-GJSA-XNiCr20-2. Basic mechanical properties, such as yield strength, tensile strength, elongation, absorbed energy and hardness, were evaluated using mechanical tests. The fatigue limit was determined using low-frequency fatigue tests. Corrosion properties, such as average corrosion rate, corrosion potential and corrosion current density, were determined by the exposure immersion test and the electrochemical potentiodynamic polarisation test. Both corrosion tests were performed in a 3.5% NaCl solution (to simulate seawater) at room temperature. The results of mechanical, fatigue and corrosion tests show that austenitic nodular cast irons have lower strength and fatigue properties but significantly higher plastic properties and corrosion resistance compared to non-austenitic nodular cast irons.

Ni-Resist, NiMn-nodular cast iron, NiCr-nodular cast iron, austenitic matrix, corrosion

Ni-Resist, NiMn-nodular cast iron, NiCr-nodular cast iron, austenitic matrix, corrosion

VAŠKO, A.; ZATKALÍKOVÁ, V.; BELAN, J.; UHRÍČIK, M.; KAŇA, V.

2025

31.05.2024

Elsevier

Procedia Structural Integrity

2452-3216

Procedia Structural Integrity

58

Kingdom of the Netherlands

48

53

6

https://www.sciencedirect.com/science/article/pii/S2452321624004384?via%3Dihub