2D MoSe2 Structures Prepared by Atomic Layer Deposition

2D MoSe2 Structures Prepared by Atomic Layer Deposition

WoS Article

Here, we demonstrate the preparation of 2D MoSe2 structures by the atomic layer deposition technique. In this work, we use ((CH3)3Si)2Se as the Se precursor and Mo(CO)6 or MoCl5 as the Mo precursors. The X-ray photoelectron spectroscopy (XPS) analyses of the prepared samples have revealed that using the MoCl5 precursor the obtained structure of MoSe2 is nearly identical to the reference powder MoSe2 sample while the composition of the sample prepared from Mo(CO)6 contains a significant amount of oxygen atoms. Further inspection of as-deposited samples via scanning electron microscopy (SEM), X-ray diffraction (XRD), and Raman spectroscopy has disclosed that the MoSe2 structure based on MoCl5 is formed from randomly oriented well crystalline flakes with their size
100nm in contrast to the Mo–Se–O compact film originating from Mo(CO)6.

Here, we demonstrate the preparation of 2D MoSe2 structures by the atomic layer deposition technique. In this work, we use ((CH3)3Si)2Se as the Se precursor and Mo(CO)6 or MoCl5 as the Mo precursors. The X-ray photoelectron spectroscopy (XPS) analyses of the prepared samples have revealed that using the MoCl5 precursor the obtained structure of MoSe2 is nearly identical to the reference powder MoSe2 sample while the composition of the sample prepared from Mo(CO)6 contains a significant amount of oxygen atoms. Further inspection of as-deposited samples via scanning electron microscopy (SEM), X-ray diffraction (XRD), and Raman spectroscopy has disclosed that the MoSe2 structure based on MoCl5 is formed from randomly oriented well crystalline flakes with their size
100nm in contrast to the Mo–Se–O compact film originating from Mo(CO)6.

atomic layer deposition, MoSe2, structure

atomic layer deposition, MoSe2, structure

KRBAL, M.; PŘIKRYL, J.; ZAZPE, R.; DVOŘÁK, F.; BUREŠ, F.; MACÁK, J.

2019

01.05.2018

1862-6254

Physica Status Solidi-Rapid Research Letters

12

5

Federal Republic of Germany

1800023-1

1800023-4

4