Detail publikačního výsledku

Chevron crack prediction using the extremely low stress triaxiality test

ŠEBEK, F.; KUBÍK, P.; PETRUŠKA, J.

Original Title

Chevron crack prediction using the extremely low stress triaxiality test

English Title

Chevron crack prediction using the extremely low stress triaxiality test

Type

Scopus Article

Original Abstract

Forward extrusion is typical way of mass-production of cold formed bars or rods with constant cross section. This process is used for production of engine alternator shafts and it is based on reducing the diameter of semi-product without removing material in several reductions. However, there is a potential danger of the chevron cracking. Chevron cracks are inside the material and therefore invisible on the surface of the semi-product. Using computational methods, the potential cracking can be predicted in advance, therefore it may lead to considerable savings. Three various phenomenological ductile fracture criteria were calibrated and then applied to forward extrusion process. As there are specific stress states in this process, new extremely low stress triaxiality fracture test were designed and used in the criteria calibration process. The test is based on the compression of the cylinder with a specific recess. Then, the criteria prediction ability and reliability is discussed.

English abstract

Forward extrusion is typical way of mass-production of cold formed bars or rods with constant cross section. This process is used for production of engine alternator shafts and it is based on reducing the diameter of semi-product without removing material in several reductions. However, there is a potential danger of the chevron cracking. Chevron cracks are inside the material and therefore invisible on the surface of the semi-product. Using computational methods, the potential cracking can be predicted in advance, therefore it may lead to considerable savings. Three various phenomenological ductile fracture criteria were calibrated and then applied to forward extrusion process. As there are specific stress states in this process, new extremely low stress triaxiality fracture test were designed and used in the criteria calibration process. The test is based on the compression of the cylinder with a specific recess. Then, the criteria prediction ability and reliability is discussed.

Keywords

forward extrusion; ductile fracture; extremely low stress triaxiality; explicit finite element method; AISI 1045

Key words in English

forward extrusion; ductile fracture; extremely low stress triaxiality; explicit finite element method; AISI 1045

Authors

ŠEBEK, F.; KUBÍK, P.; PETRUŠKA, J.

RIV year

2016

Released

03.06.2015

ISBN

1803-1269

Periodical

MM Science Journal

Number

June

State

Czech Republic

Pages from

617

Pages to

621

Pages count

5

Full text in the Digital Library

http://hdl.handle.net/

BibTex

@article{BUT114704,
  author="František {Šebek} and Petr {Kubík} and Jindřich {Petruška}",
  title="Chevron crack prediction using the extremely low stress triaxiality test",
  journal="MM Science Journal",
  year="2015",
  number="June",
  pages="617--621",
  doi="10.17973/MMSJ.2015\{_}06\{_}201518",
  issn="1803-1269"
}