Influence of graphite materials S18, S19 and S20 on properties of positive electrodes

CHLADIL, L.

Original Title

Influence of graphite materials S18, S19 and S20 on properties of positive electrodes

English Title

Influence of graphite materials S18, S19 and S20 on properties of positive electrodes

Type

Summary research report

Original Abstract

This report contains measurement results of electrodes which contain 20% of graphite samples labelled S18, S19 and S20 from company AMG mining AG. Electrodes were prepared with the Ni(OH)2 which is used by customers of AMG mining AG. These materials were measured in cells with a large excess of electrolyte by galvanostatic cycling. The measurements were repeated after 10 -day ageing at elevated temperature at constant voltage 1.3 V. Commercial cadmium material labelled Kans G was used as negative electrode.

English abstract

This report contains measurement results of electrodes which contain 20% of graphite samples labelled S18, S19 and S20 from company AMG mining AG. Electrodes were prepared with the Ni(OH)2 which is used by customers of AMG mining AG. These materials were measured in cells with a large excess of electrolyte by galvanostatic cycling. The measurements were repeated after 10 -day ageing at elevated temperature at constant voltage 1.3 V. Commercial cadmium material labelled Kans G was used as negative electrode.

Keywords

Graphite, ageing, nickel hydroxide,

Authors

CHLADIL, L.

Released

06.06.2013

Pages count

39

BibTex

@misc{BUT108798,
  author="Ladislav {Chladil}",
  title="Influence of graphite materials S18, S19 and S20 on properties of positive electrodes",
  year="2013",
  pages="39",
  note="Summary research report"
}