Hydrogen embrittlement induced in bearing steel by electric erosion

ŠVEJCAR, J.; FORET, R.

Originální název

Hydrogen embrittlement induced in bearing steel by electric erosion

Anglický název

Hydrogen embrittlement induced in bearing steel by electric erosion

Druh

Článek recenzovaný mimo WoS a Scopus

Originální abstrakt

The subject of analysis was a spherical-roller bearing which had to be dividet into halves by using of electrospark erosion.On the cutting surfaces of the rings defects were found.On the basis of microfractographic analysis was possible to arrive at a definite assumption that this was one of clasical manifestation of hydrogen embrittlement(delayed fracture) resulting from the combined effect of hydrogenation of subsurface layers during electroerosion and residual stress

Anglický abstrakt

The subject of analysis was a spherical-roller bearing which had to be dividet into halves by using of electrospark erosion.On the cutting surfaces of the rings defects were found.On the basis of microfractographic analysis was possible to arrive at a definite assumption that this was one of clasical manifestation of hydrogen embrittlement(delayed fracture) resulting from the combined effect of hydrogenation of subsurface layers during electroerosion and residual stress

Klíčová slova

dealayed fractures; electrospark erosion; bearings

Klíčová slova v angličtině

dealayed fractures; electrospark erosion; bearings

Autoři

ŠVEJCAR, J.; FORET, R.

Rok RIV

2011

Vydáno

01.03.2010

Nakladatel

HF TU Košice

Místo

Košice,SR

ISSN

1335-1532

Periodikum

Acta Metallurgica Slovaca

Svazek

1

Číslo

2H

Stát

Slovenská republika

Strany od

99

Strany do

103

Strany počet

5

BibTex

@article{BUT50395,
  author="Jiří {Švejcar} and Rudolf {Foret}",
  title="Hydrogen embrittlement induced in bearing steel by electric erosion",
  journal="Acta Metallurgica Slovaca",
  year="2010",
  volume="1",
  number="2H",
  pages="99--103",
  issn="1335-1532"
}