Detail publikačního výsledku

Wire Arc Additive Manufacturing (WAAM) and microstructural analysis of Magnesium parts

SENCK, S.; HOLZLEITNER, M.; GLINZ, J.; MILORADOVIC, A.; KASTNER, J.; KOUTNY, D.; GNEIGER, S.

Originální název

Wire Arc Additive Manufacturing (WAAM) and microstructural analysis of Magnesium parts

Anglický název

Wire Arc Additive Manufacturing (WAAM) and microstructural analysis of Magnesium parts

Druh

Stať ve sborníku mimo WoS a Scopus

Originální abstrakt

In this contribution we used a Mg-Al-Zn-Ca alloy (AX13) that is characterized by a high aluminium content of 12-15 wt.%. When produced by AM process, this alloy achieves high yield strength, which can be further increased by artificial aging. AX13 wire was produced via casting and subsequent direct extrusion at Light Metals Technologies Ranshofen. WAAM was carried out by a gas-metal arc-welding cold metal transfer (CMT) process (Fronius, Pettenbach, Austria). Using a layer thickness of ca. 2.5 mm a total wall thickness of 5 mm was achieved. A test sample with a dimension of approximately 35 x 40 x 64 mm was extracted from a larger sample and scanned using a Rayscan 250 E system at a voxel size of 40 μm.

Anglický abstrakt

In this contribution we used a Mg-Al-Zn-Ca alloy (AX13) that is characterized by a high aluminium content of 12-15 wt.%. When produced by AM process, this alloy achieves high yield strength, which can be further increased by artificial aging. AX13 wire was produced via casting and subsequent direct extrusion at Light Metals Technologies Ranshofen. WAAM was carried out by a gas-metal arc-welding cold metal transfer (CMT) process (Fronius, Pettenbach, Austria). Using a layer thickness of ca. 2.5 mm a total wall thickness of 5 mm was achieved. A test sample with a dimension of approximately 35 x 40 x 64 mm was extracted from a larger sample and scanned using a Rayscan 250 E system at a voxel size of 40 μm.

Klíčová slova

Magnesium alloy; Wire Arc Additive Manufacturing; Microcomputed Tomography; Porosity; Inclusions

Klíčová slova v angličtině

Magnesium alloy; Wire Arc Additive Manufacturing; Microcomputed Tomography; Porosity; Inclusions

Autoři

SENCK, S.; HOLZLEITNER, M.; GLINZ, J.; MILORADOVIC, A.; KASTNER, J.; KOUTNY, D.; GNEIGER, S.

Rok RIV

2025

Vydáno

02.03.2023

Nakladatel

https://www.ndt.net/

Místo

Fürth, Germany

Kniha

12th Conference on Industrial Computed Tomography

Edice

iCT 2023

ISSN

1435-4934

Periodikum

E-Journal of nondestructive testing

Svazek

28

Číslo

3

Stát

Spolková republika Německo

Strany počet

5

URL

https://www.ndt.net/search/docs.php3?id=27724

BibTex

@inproceedings{BUT187580,
  author="SENCK, S. and HOLZLEITNER, M. and GLINZ, J. and MILORADOVIC, A. and KASTNER, J. and KOUTNY, D. and GNEIGER, S.",
  title="Wire Arc Additive Manufacturing (WAAM) and microstructural analysis of Magnesium parts",
  booktitle="12th Conference on Industrial Computed Tomography",
  year="2023",
  series="iCT 2023",
  journal="E-Journal of nondestructive testing",
  volume="28",
  number="3",
  pages="5",
  publisher="https://www.ndt.net/",
  address="Fürth, Germany",
  doi="10.58286/27724",
  url="https://www.ndt.net/search/docs.php3?id=27724"
}