Publication detail

Properties od alkali-activated aluminosilicate materials after high temperature load.

ROVNANÍKOVÁ, P., BAYER, P., PAVLAS, R.

Original Title

Properties od alkali-activated aluminosilicate materials after high temperature load.

English Title

Properties od alkali-activated aluminosilicate materials after high temperature load.

Type

conference paper

Language

en

Original Abstract

This paper reports the results of an investigation on changes of compounds of alkali-activated aluminosilicates materials at high temperatures. The mixtures for testing specimens were composed of fine ground granulated blast furnace slag and dried sodium silicate (water glass) of silicate modulus Ms = 2.07. The materials were tested after 200, 400, 600, 800, 1000 and 1200°C. The compounds formed at high temperatures were identified by X-ray diffraction analysis, thermal analysis and mercury porosimetry.

English abstract

This paper reports the results of an investigation on changes of compounds of alkali-activated aluminosilicates materials at high temperatures. The mixtures for testing specimens were composed of fine ground granulated blast furnace slag and dried sodium silicate (water glass) of silicate modulus Ms = 2.07. The materials were tested after 200, 400, 600, 800, 1000 and 1200°C. The compounds formed at high temperatures were identified by X-ray diffraction analysis, thermal analysis and mercury porosimetry.

Keywords

Alkali-activated, slag,high, temperature

RIV year

2002

Released

01.01.2002

Location

Brno

ISBN

80-214-2130-4

Book

Non-Traditional Cement and Concrete

Issue number

1.

Pages from

43

Pages to

51

Pages count

9

Documents

BibTex 


@inproceedings{BUT10592,
  author="Pavla {Rovnaníková} and Patrik {Bayer} and Radek {Pavlas}",
  title="Properties od alkali-activated aluminosilicate materials after high temperature load.",
  annote="This paper reports the results of an investigation on changes of compounds of alkali-activated aluminosilicates materials at high temperatures. The mixtures for testing specimens were composed of fine ground granulated blast furnace slag and dried sodium silicate (water glass) of silicate modulus Ms = 2.07. The materials were tested after 200, 400, 600, 800, 1000 and 1200°C. The compounds formed at high temperatures were identified by X-ray diffraction analysis, thermal analysis and mercury porosimetry.",
  booktitle="Non-Traditional Cement and Concrete",
  chapter="10592",
  year="2002",
  month="january",
  pages="43",
  type="conference paper"
}